90% Ti, 6% V, 4% Others, Highly Biocompatible Type IV
Advantages
- Innovative material, grade 23 titanium
- Highly biocompatible
- Low specific weight
- Optimal modulus of compatibility for a more stable result
Indications
- Telescopic and conus crowns
- Full contour crowns
- Implant born bars
- Partial denture frames
- Porcelain substructures
Composition
Ti 90.0
Al 6.0
V 4.0
Fe < 1.0
Technical data
| Solidus-liquidus temperature | 1605 -1660°C |
| Melting point | 1710°C |
| Density | 4426 g/cmc |
| Vickers hardness | 312 HV10 |
| Percentage elongation at fracture | 14% |
| Yield load strength (Rp0.2) | (Rp0.2) 880 MPa |
| Modulus of elasticity | 114 GPa |
| Color | White |